- HDPE[6]
- LDPE[1]
- LLDPE[1]
- PP[8]
- Recycled Plastic[3]
- ABS[6]
- PC[7]
- HIPS[2]
- EPS[1]
- PS[3]
- Other Plastic Products[1]
- PVC[7]
- PET[7]
- PMMA[7]
- PBT[6]
- PA[7]
- PTFE[7]
- EVA[7]
- POM[7]
- PPO[7]
- EPDM[6]
- Other Rubber Products[1]
- TPU[5]
- Other Plastic Raw Materials[1]
- Chemical Auxiliary Agent[1]
- Plastic Masterbatches[5]
- Contact Person : Ms. Liu Anita
- Company Name : Dongguan Heyue Import And Export Co., Ltd.
- Tel : 86-769-82337156
- Fax : 86-769-87787158
- Address : Guangdong,Dongguan,Room F-210,Business Office Building,South Automobile Expo Center 2nd Floor,Zhangmutou Town
- Country/Region : China
PA6/PA66 RESIN Nylon 6/Nylon66 30%GF reinforced
PA6/PA66 RESIN Nylon 6/Nylon66
Packaging & Delivery
Packaging Detail: | Net Weight / Bag: 25KG |
Delivery Detail: | within 2 weeks after receive advance payment |
Specifications
Super Tough,Very Flexible,Lubricated PA6 Offers High ProductivityLow Temperature ToughnessDown to -40 CSGS Inspection
Impact modified PA6 resin, Available in natural and black.Super Tough, high performance polyamide 6 resin. It offers outstanding molding performance in injection molding applications. High shock resistance even in the dry state and at low temperatures .
TEST ITEMS | TEST METHOD AND CONDITIONS | TEST RESULTS | |||||
TEST METHOD | UNIT | CONDITIONS | |||||
(DRY)23 | |||||||
Density | ISO1183 | g/cm3 | 1.08 | ||||
Melt Volume Rate | ISO1133 | cc/10min | (275)2.16kg | 5.4 | |||
Tensile Strength | ISO527 | MPa | 10mm/min | 49 | |||
Tensile strain at break | ISO527 | % | 167 | ||||
Flexural Strength | ISO178 | MPa | 49 | ||||
Flexural Modulus | ISO178 | MPa | 1,500 | ||||
Charpy Notched | ISO179 | KJ/m2 | 2.9m/s-1J | 38 | |||
Izod Notched Impact | ISO180 | KJ/m2 | 3.5m/s-1J | 51 | |||
Flame resistance | UL-94 | HB | |||||
Ash content | % | 0 | |||||
Processing Guidelines | |||||||
Material HandlingMax. Water content: 0.12%Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficient | |||||||
Typical ProfileMelt Temperature 220-250°C (428-482 °F)Mold Temperature 60-90 °C (158-194 °F)Injection and Packing Pressure 35-125 bar (500-1500 psi) | |||||||
Fill RateFast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate | |||||||
PA6/PA66 RESIN Nylon 6/Nylon66 30%GF reinforced